Machida, Hideo*; Koizumi, Yu*; Wakai, Takashi; Takahashi, Koji*
Nihon Kikai Gakkai M&M 2019 Zairyo Rikigaku Kanfarensu Koen Rombunshu (Internet), p.OS1307_1 - OS1307_5, 2019/11
This paper describes the fracture test and fracture analysis of a pipe under displacement control load. In order to grasp the fracture behavior of the circumferential through-wall cracked pipe, which is important in evaluating the feasibility of leak before break (LBB) in sodium cooled reactor piping, a fracture test in case of a circumferential throughwall crack in the weld line between an elbow and a straight pipe was carried out. From this test, it was found that no pipe fracture occurs in the displacement control loading condition even if a large circumferential through-wall crack (180) was assumed. The fracture analysis of the pipe was carried out using Gurson's parameters set based on the tensile test results of the tested pipe material. The analytic results agree well with the test results, and it was found that it will be possible to predict the fracture behavior of sodium cooled reactor piping.